Luminescent Phosphor-in-Glass Composite for White Light-Emitting Diodes

1ITMO University, Saint-Petersburg, Russia

2Ioffe Institute, Saint-Petersburg, Russia


Journal of Optoelectronics Engineering. 2017, Vol. 5 No. 1, 7-9
DOI: 10.12691/joe-5-1-2
Copyright © 2017 Science and Education Publishing

Cite this paper:
M.A. Kistankina, V.A. Aseev, J.V. Tuzova, K.D. Mynbaev, V.E. Bougrov, N.V. Nikonorov, A.E. Romanov. Luminescent Phosphor-in-Glass Composite for White Light-Emitting Diodes. Journal of Optoelectronics Engineering. 2017; 5(1):7-9. doi: 10.12691/joe-5-1-2.

Correspondence to: M.A.  Kistankina, ITMO University, Saint-Petersburg, Russia. Email: shvalevama@niuitmo.ru

Abstract

A luminescent composite material based on YAG:Ce3+–doped silicate glass (Phosphor-in-Glass, PiG) was fabricated and studied. For the glass matrix, the 40SiO2–25PbF2–20PbO(Pb3O4)–15AlF3 material was used. PiG samples were sintered at the temperature 550°C with concentration of YAG:Ce3+ varying from 90% down to 50%. Luminescence spectra of the PiG samples were recorded and quantum efficiency of the experimental samples was measured with the use of an integrating optical sphere. A design of light-emitting diode (LED) modules with the sintered PiG was developed and the temperature of the surface of the modules was analyzed.