Dear Label_Name,

Greetings! I hope you are well.

I am writing on behalf of an international publishing house, Science and Education Publishing, USA (http://www.sciepub.com).

Science and Education Publishing (SciEP) is a multidisciplinary open access publisher of Journals covering the fields of Science, Technology and Medicine. All SciEP publications are subject to high-quality peer review, editorial and production processes and are freely available online.

Welcome to the April, 2013 edition of SciEP newsletter, providing monthly summaries of articles on science & education related topics of interest to scientist and professionals. The mission of our journals is to provide an open access forum for publishing new findings on issues pertinent to scientific and academic field. We also invite you to submit original research papers, review articles, short reports, or case studies are considered for publication in our Multidisciplinary Journals.

American Journal of Public Health Research
DOI: 10.12691/ajphr-1-1-3

The Implementation of a Tele-Homecare System with Service Oriented Architecture and HL7 Message Transmission Standard
Ching-Sung Wang

American Journal of Medical and Biological Research
DOI: 10.12691/ajmbr-1-1-2

The Influence of Ethanol on Pyruvate Kinases Activity in Vivo, in Vitro, in Silico
Lelevich Sergey Vladimirovich, Khrustalev Vladislav Victorovich, Barkovsky Eugene Victorovich, Shedogubova Tatyana Aleksandrovna

American Journal of Medical Sciences and Medicine
DOI: 10.12691/ajmsm-1-1-1

Clinical and Histological Features in Wegener Granulomatosis
Li Cavoli Gioacchino, Passantino Rita, Bono Luisa, Tortorici Calogera, Ferrantelli Angelo, Giammarresi Carlo, Rotolo Ugo

American Journal of Infectious Diseases and Microbiology
DOI: 10.12691/ajidm-1-1-2

The Curse of Lymphatic Filariasis: Would the Continual Use of Diethylcarbamazine Eliminate this Scourge in Papua New Guinea?
Anne Lanham, Lillian Mwanri

We have released issues of some journals on February 2013.
American Journal of Public Health Research
American Journal of Medical Sciences and Medicine
American Journal of Medical and Biological Research
American Journal of Pharmacological Sciences
American Journal of Clinical Medicine Research
American Journal of Nursing Research
American Journal of Cancer Prevention
American Journal of Medicine Studies
American Journal of Infectious Diseases and Microbiology
American Journal of Cardiovascular Disease Research
American Journal of Biomedical Research
American Journal of Mechanical Engineering
American Journal of Microbiological Research
Journal of Preventive Medicine
American Journal of Food and Nutrition
American Journal of Hypertension Research
American Journal of Sports Science and Medicine
Journal of Cancer Research and Treatment
American Journal of Zoological Research
Journal of Biomedical Engineering and Technology
American Journal of Microbiological Research
Biomedical Science and Engineering

We are pleased to announce that submissions are now being accepted for peer review for all the journals across all our subject areas in SciEP.

Please submit your manuscript via our online submission system:
http://www.sciepub.com/author/signin

To unsubscribe from our mailing list, please click on the following link: unsubscribe

I am looking forward to hearing from you.

Kind regards,

David Rain
Email:join@sciepub.com
Science and Education Publishing (http://www.sciepub.com)

Precipitation Behavior in an Al-Mg Alloy with High Mg Composition

Takuya Yako, Koichiro Fukui, Mao Naito, Mahoto Takeda*

Department of Materials Engineering, Yokohama National University, Yokohama 240-8501, Japan

Abstract: We have investigated the precipitation phenomena which occur at high aging temperatures in an Al-Mg alloy with high Mg concentration by means of Vickers hardness (HV) testing, differential scanning calorimetry (DSC), transmission electron microscopy (TEM) and analytical scanning transmission electron microscopy (STEM-EDX). It was found that the hardness and heat changes are closely correlated, and that the size of the exothermic heat peak depends on the quantity of β'- phase formed during isothermal aging prior to the DSC measurements. This implies that the formation of β'-phase precipitates is mainly responsible for the increase in hardness. Our TEM observations showed that β'-phase precipitates are plate-like in morphology and form on matrix {100}planes, whilst stable β-phase precipitates are granular in shape. In-situ TEM using a heating holder revealed that β-phase precipitates grew by consumption of β'-phase platelets. Element-maps obtained by STEM-EDX indicated that the composition of β'-phase platelets was approximately Al-33at%Mg.

Keywords: aluminum-magnesium alloy, precipitation, isothermal aging, Vickers microhardness, differential scanning calorimetry, transmission electron microscopy

Received June 14, 2018; Revised August 21, 2018; Accepted August 26, 2018

Citation: Takuya Yako, Koichiro Fukui, Mao Naito, Mahoto Takeda, Precipitation Behavior in an Al-Mg Alloy with High Mg Composition. Materials Science and Metallurgy Engineering, 5 (1). 1-4. January 2018. doi:10.12691/msme-5-1-1

1. Introduction

Aluminum-base Al-Mg alloys are well-known light-weight metallic materials possessing high strength and good corrosion resistance, which make them versatile in various practical applications. As the Mg composition increases, the strength of the alloy increases but the workability decreases. The deterioration of workability causes difficulties in production and usage [1]. Previous studies have claimed that precipitation hardening occurs in Al-Mg alloys with a Mg content more than ~ 6wt%, while in alloys containing less than ~ 6wt%Mg the mechanism is solid-solution hardening [2,3]. However, this conclusion is still under discussion, because of insufficient knowledge of how the atomic composition, the annealing temperature and the diffusivity of Mg atoms affect phase decomposition.

A variety of precipitation phenomena have been reported in Al-Mg alloys. Precipitates have been found to form both inside grains and at grain boundaries during high-temperature aging [4,11]. Other structural changes such as the formation of GP zones, and modulated and ordered structures have been reported in alloys annealed at low temperatures [5,6,7]. The crystal structures of stable β-phase and metastable β'-phase have been previously investigated. However, the details of phase decomposition in Al-Mg alloys are still not fully understood [8,9,10]. Since both solid-solution and precipitation strengthening are important in Al-Mg alloys, the mechanisms should be examined more in detail. The present work investigates precipitation in an Al-13.7at%Mg aged at 473K.

2. Experimental Procedure

We examined an Al-13.7at% Mg alloy, using a Shimadzu HMV-2000 Vickers hardness tester, a RIGAKU Thermoplus 8230 differential scanning calorimeter (DSC), a HITACHI H-800 transmission electron microscope (TEM) and a JEOL 2100F scanning transmission electron microscope equipped with an energy-dispersive X-ray spectrometer (STEM-EDX).

The samples were homogenized by annealing at 723K in a salt bath (KNO₃: NaNO₃ = 1:1 in molar ratio) for 4320 min. They were then solution-treated at 723K for 60 min and quenched in ice water. Subsequently, the samples were aged isothermally either at 373K or at 473K in an oil bath. The size of samples for HV measurement was 10 mm × 10 mm × 1.5 mm, and the surface was polished slighly with emery #2000 paper. DSC measurements were performed from room temperature to 723 K at a rate of 2K / min. The samples for conventional TEM were punched out as disks with a diameter of 3 mm, and the disks were electro-polished after heat treatments. The samples for STEM-EDX were prepared using an elctro-polisher and a focussed ion-beam thinner.

3. Results and Discussion

3.1. Vickers Hardness Tests

Figure 1 shows the changes in the Vickers hardness (HV) due to isothermal aging. At an aging temperature of 373K, the Vickers hardness started to increase after aging for 2×10⁴ min and continued to increase to the maximum aging time of 106 min. In the specimen aged at 473K, the hardness increased after only 30 min to reach a peak hardness of HV =138.2 after 500 min. The hardness then remained close to this value before falling off after about 5000 min due to overaging.

The overall trends seen in these curves - that the maximum value of the HV hardness occurs at longer aging times at the lower aging temperature, but the HV hardness attains a higher value - are commonly observed in precipitation-hardened aluminum alloys. Unlike other Al-base precipitation alloys, however, overaging after the peak condition did not occur rapidly in the Al-13.7at%Mg annealed at 473K: the hardness kept at a high level for a relatively long period. This fact suggests that the diffusion of Mg atoms in the aluminum-rich matrix does not occur easily.

Figure 1. The Vickers hardness vs. aging time curves obtained for Al-13.7at%Mg alloy samples isothermally aged at 373K and 473K, respectively.

3.2. DSC Measurements

DSC thermograms of Al-13.7at%Mg specimens aged for various times at 473K are shown in Figure 2.

Figure 2. DSC curves of Al-13.7at%Mg samples isothermally aged at 473K for various times

Exothermic peaks appearing above the horizontal axis and endothermic peak below the axis represent the formation and dissolution of stable/ quasistable phases, respectively. An endothermic peak due to clustering is observed at 320-350K. Exothermic/endothermic peaks appeared around 470-520K are likely due to precipitation of the β'-phase [9,12]. Another exothermic peak corresponding to the precipitation of the β-phase is observed in the vicinity of 560K. The heights of the exothermic peaks due to the formation β'- and β-phases decreased with increasing aging time. This trend suggests that both types of precipitates formed during the isothermal aging prior to the DSC measurements. The reduction of the heat Δh corresponds to the amount of precipitation as was observed in Al-Mg-Si alloys [13]. To estimate the amount of the β'- and β-phases transformations in this Al-Mg alloy quantitatively in a similar manner to the previous work, we separated the two exothermic peaks appearing around 460-600K, using a commercial software package, “Origin”.

Figure 3 shows the relationships between the Δh(β'), Δh(β) and the aging time, respectively. The aging time at which the heat change started to increase coincides with the onset time of the increase in HV hardness. Thus, comparing the heat reductions ∆h(β') and Δh(β) with the Vickers hardness, we conclude that the precipitation of β' - and β-phases were responsible for the increase in hardness, but the precipitation of β'-phase is likely to be more important.

Figure 3. Heats of metastable and stable precipitates estimated from DSC measurements of Al-13.7at%Mg samples aged at 473K for various times

3.3. TEM Observations

TEM was carried out to investigate microstructural evolution in specimens aged both at 373K and at 473K. Figure 4 shows two TEM micrographs of the same area in a sample aged at 373K for 1×10⁵ min taken from the <001> and <110> zone axes of the aluminum matrix, respectively. In the TEM micrograph taken from the <001> direction, precipitates appear needle-like with lengths of the order of microns along <100> directions but with negligible width, while in the micrograph taken from the <110> direction they seem plate-like with considerable width. These observations are consistent with platelet precipitates lying on matrix {100} planes, which are edge-on when viewed from the <001> direction.

Figure 4. Bright-field TEM images of an Al-13.7at%Mg alloy sample taken from 100 and (b) 110 zones, after aging at 373K for 1×10⁵ min

TEM micrographs of samples aged at 473K for various times from 10 min to 500 min are shown in Figure 5. They show that β'-phase precipitates were formed in the matrix at these aging conditions. Precipitates were initially granular, but transformed into a plate-like precipitates, and finally turned into thick rod-shaped precipitates with increasing aging time.

Figure 5. Microstructures of Al-13.7at%Mg alloy aged at 473K for (a) 10 min, (b) 50 min, (c) 100 min and (d) 500 min, respectively

In order to distinguish the shapes of β'- and β-phases precipitates, we examined the microstructure of samples aged at the condition that the exothermal peak fell down to the horizontal line in the DSC insrument. Figure 6 shows TEM images of the microstrocture taken from <100> and <110> zones of the matrix. The TEM observations revealed that β-phase precipitates are thick granules with ireguralr shapes.

Figure 6. Bright-field TEM images of Al-13.7at%Mg alloy taken from (a) <100> and (b) <110> zones, after aging up to 570K in the DSC

3.4. In-situ TEM Observations of Microstructural Evolution in an Al-Mg Alloy Aged at 473 K

To investigate the structural sequence of the β'- and β-phases, we conducted in-situ TEM heating experiments on as-quenched samples. Figure 7 shows two TEM images of the same area of a sample receiving (a) aging at 473 K for 80 min, and (b) after further in-situ aging at 473 K totally for 500 min.

Figure 7. Bright-field TEM images of Al-13.7at%Mg aged at 473K for (a) 80 min and (b) 500 min, respectively

In these TEM images, two types of precipitates may be seen: small needle-like particles, densely distributed; and large precipitates with irregular shapes. The large precipitates were observed to grow, and nearby small precipitates to shrink, so that precipitation-free zones formed around the large precipitates. These observations strongly suggest that the large precipitates grew and coarsened by absorbing solute atoms released by the small particles. We conclude that the small and large precipitates are the β'- and β-phases, respectively, and that the β'- and β-phases are independent from each other with respect to crystallographic structure and thermal stability.

3.5. STEM-EDX Observations on β'-phase Precipitates

Several quasi-stable precipitates with different structures and compositions may form during the phase decomposition of Al-Mg alloys, depending on the aging temperature. In this section, we describe results obtained using STEM-EDX. Since TEM samples were prepared by combination of elecro-polishing and ion-beam thinning, β' -phase precipitates often protruded from the sample edge of the thin-film region. Figure 8 shows protruding platelets of β'-phase precipitates in an Al-13.1at%Mg sample aged isothermally at 473K for 1000min. The matrix effect was thus minimized in the composition analysis in this area.

Figure 8. β'-phase precipitates of an Al-13.7at%Mg sample isothermally aged at 473K for 1000 min

Figure 9 (a) and (b) show STEM-EDX compositional maps of this area for Al and Mg, respectively. These maps confirm that Mg is concentrated in the β'-phase. Quantitative analysis shows that the average Mg concentrations were 33at% for the precipitates and approximately 7% for the matrix. This result may be feasible, since it is intermediate between the stable β-phase of Al₃Mg₂ (Mg: 40at%) and GP zones of Al₃Mg (Mg: 25at%).

Figure 9. STEM-EDX element maps of Al-13.7at%Mg alloy sample aged at 473K for 1000 min. The left and right images were Al-K and Mg-K spectral maps, respectively

In section 3.1 above, we discussed the changes in Vickers hardness during the isothermal aging, and concluded that precipitation in this Al-Mg alloy was relatively slow. The TEM observations here, which show that β'-phase precipitates are subject to Mg diffusion in the matrix, suggest that the slow precipitation is due to low diffusivity of Mg in Al.

4. Conclusions

We have investigated precipitation behavior in an Al-13.7at%Mg alloy, using Vickers micro-hardness testing, TEM and DSC. The following conclusions were obtained:

(1) The correlation between the hardness changes and heat changes, Δh, in the DSC curves implies that the main contribution to the increase in hardness on aging is β'-phase formation.

(2) TEM observations indicated that β'-phase precipitates form on the {001} planes of the Al matrix and grow along the <001> direction in the early stage of aging at both 373K and 473K. The composition of the β'-phase precipitates is approximately 33at%Mg.

(3) The relatively slow rate of precipitation in this Al-Mg alloy is caused by low diffusivity of Mg atoms in the aluminum matrix.

Acknowledgements

The authors acknowledged Drs. H. Yoshida and H. Tanaka of The UACJ Co., Japan for providing Al-Mg alloy ingots for this study. The authors are also grateful to Emeritus Professor Michael Jenkins of Trinity College, Oxford for critical reading and valuable comments.

References

[1]   | M. Otsuka, R. Horiuchi, “Ductility loss of Al-Mg alloys at high temperatures,“ Japan Institute of Metals, 48 (7), 688-693, 1984.
[2]   | E.C.W. Perryman and G.B. Brook. “Mechanism of precipitation in aluminum-magnesium alloys“, J. Inst. Metals, 79, 19-34. 1951
[3]   | M.Kubota, J.F. Nie and B.C.Muddle, “Characterization of precipitation hardening response and as-quenched microstructures in Al-Mg(-Ag) alloys”, Mat. Trans., 45(12), 3256-3263, 2004.
[4]   | S. Osaki, Y. Kojima, T. Takahashi, “Stress corrosion cracking and intergranular corrosion of 5083 aluminum alloy”, Japan Institute of Light Metals, 25 (5) 173-178, 1975.
[5]   | T. Takahashi, T. Sato, “Formation of a modulated structure and an ordered structure in concentrated Al-10% and 14%Mg alloys”, Japan Institute of Metals, 50 (2), 133-140, 1986.
[6]   | K. Osamura and T. Ogura, “Metastable phases in the early stage of precipitation in Al-Mg alloys”, Metall. Trans., 15A (5), 835-842, May. 1984.
[7]   | T. Sato, Y. Kojima and T. Takahashi, “Modulated structures and GP zones in Al-Mg alloys”, Metall. Trans., 13A (8), 1373-1378, Aug. 1982.
[8]   | S. Nebti, D. Hamana and G. Cizeron, “Calorimetric study of pre-precipitation and precipitation in Al-Mg alloy”, Acta Metall. Mater., 43 (9), 3583-3588, 1995.
[9]   | M. J. Starink and A.-M. Zahra, “β' and β precipitation in an Al-Mg alloy studied by DSC and TEM”, Acta Mater., 46(10), 3381-3397, Jun. 1998.
[10]   | M. J. Starink and A.-M. Zahra, “Precipitation kinetics of an Al-15%Mg alloy studied by microcalorimetry and TEM”, Mater. Sci. Forum, 217-222, 795-800, 1996.
[11]   | H. Inagaki, “Precipitation of the β-phase in Al-Mg alloys”, Z. Metallkd., 96 (1), 45-53, 2005.
[12]   | R. Nozato, S. Ishihara, “Calorimetric study of precipitation process in Al-Mg alloys”, Transactions of the Japan Institute of Metals, 21 (9), 580-588, 1980.
[13]   | K. Fukui, M.Takeda, T.Endo, “Morphology and thermal stability of metastable precipitates formed in an Al-Mg-Si ternary alloy aged at 403K to 483K”, Materials Lett., 59 (11), 1444-1448, 2005.