Dear Label_Name,

Greetings! I hope you are well.

I am writing on behalf of an international publishing house, Science and Education Publishing, USA (http://www.sciepub.com).

Science and Education Publishing (SciEP) is a multidisciplinary open access publisher of Journals covering the fields of Science, Technology and Medicine. All SciEP publications are subject to high-quality peer review, editorial and production processes and are freely available online.

Welcome to the April, 2013 edition of SciEP newsletter, providing monthly summaries of articles on science & education related topics of interest to scientist and professionals. The mission of our journals is to provide an open access forum for publishing new findings on issues pertinent to scientific and academic field. We also invite you to submit original research papers, review articles, short reports, or case studies are considered for publication in our Multidisciplinary Journals.

American Journal of Public Health Research
DOI: 10.12691/ajphr-1-1-3

The Implementation of a Tele-Homecare System with Service Oriented Architecture and HL7 Message Transmission Standard
Ching-Sung Wang

American Journal of Medical and Biological Research
DOI: 10.12691/ajmbr-1-1-2

The Influence of Ethanol on Pyruvate Kinases Activity in Vivo, in Vitro, in Silico
Lelevich Sergey Vladimirovich, Khrustalev Vladislav Victorovich, Barkovsky Eugene Victorovich, Shedogubova Tatyana Aleksandrovna

American Journal of Medical Sciences and Medicine
DOI: 10.12691/ajmsm-1-1-1

Clinical and Histological Features in Wegener Granulomatosis
Li Cavoli Gioacchino, Passantino Rita, Bono Luisa, Tortorici Calogera, Ferrantelli Angelo, Giammarresi Carlo, Rotolo Ugo

American Journal of Infectious Diseases and Microbiology
DOI: 10.12691/ajidm-1-1-2

The Curse of Lymphatic Filariasis: Would the Continual Use of Diethylcarbamazine Eliminate this Scourge in Papua New Guinea?
Anne Lanham, Lillian Mwanri

We have released issues of some journals on February 2013.
American Journal of Public Health Research
American Journal of Medical Sciences and Medicine
American Journal of Medical and Biological Research
American Journal of Pharmacological Sciences
American Journal of Clinical Medicine Research
American Journal of Nursing Research
American Journal of Cancer Prevention
American Journal of Medicine Studies
American Journal of Infectious Diseases and Microbiology
American Journal of Cardiovascular Disease Research
American Journal of Biomedical Research
American Journal of Mechanical Engineering
American Journal of Microbiological Research
Journal of Preventive Medicine
American Journal of Food and Nutrition
American Journal of Hypertension Research
American Journal of Sports Science and Medicine
Journal of Cancer Research and Treatment
American Journal of Zoological Research
Journal of Biomedical Engineering and Technology
American Journal of Microbiological Research
Biomedical Science and Engineering

We are pleased to announce that submissions are now being accepted for peer review for all the journals across all our subject areas in SciEP.

Please submit your manuscript via our online submission system:
http://www.sciepub.com/author/signin

To unsubscribe from our mailing list, please click on the following link: unsubscribe

I am looking forward to hearing from you.

Kind regards,

David Rain
Email:join@sciepub.com
Science and Education Publishing (http://www.sciepub.com)

Effect of TiO₂ Photoanode Films on the Performance of Dye Sensitized Solar Cell with Rauvolfia Vomitoria Fruit Extract

J. K. Datte*, S. A. Yapi, L. K. Kouassi, G. Y. T. Douhoré

Laboratoire de Physique de la matière condensée et technologie (LPMCT), Université Félix Houphouët Boigny, Abidjan-Cocody, Côte d’Ivoire

Abstract: Dye sensitized solar cells (DSSC) were investigated using Rauvolfia vomitoria fruit extract as natural sensitized of TiO₂ thin film. The cells were evaluated for various thicknesses of photoanode. The optical properties were analysed with UV-Vis spectroscopy and Fourier Transform Infrared spectroscopy (FT-IR). The morphology of the TiO₂ surface was observed with a scanning electron microscope (SEM). Energy levels were estimated by cyclic voltammetry, in the presence of tetrabutalamonium tetrafluoroborate (TBATFB), in anhydrous acetonitrile solution (ACN). The results showed that the optimum thickness is 10 μm which achieved a short-circuit current density (Jsc) of 0.1 mA/cm² and an open voltage (Voc) of 0.65 V while the conversion efficiency ) is 0.055%.

Keywords: DSSC, natural dye, photoanode thickness, energy conversion, efficiency

Received January 02, 2021; Revised January 16, 2021; Accepted January 25, 2021

Citation: J. K. Datte, S. A. Yapi, L. K. Kouassi, G. Y. T. Douhoré, Effect of TiO₂ Photoanode Films on the Performance of Dye Sensitized Solar Cell with Rauvolfia Vomitoria Fruit Extract. American Journal of Materials Science and Engineering, 9 (1). 1-5. January 2021. doi:10.12691/ajmse-9-1-1

1. Introduction

Dye-sensitized solar cells belong to a new generation of photovoltaic conversion materials. These cells were developed by Grätzel and O’Regan [1]. The cells include two electrodes, a photoanode and a photocathode made from transparent conductive oxide (TCO). TiO₂, a porous semiconductor, was coated on the photoanode, which allowed to fix the dye or sensitizer. The sensitizer absorbed the sunlight. A platinum thin-film was coated on the photocathode and acted as a catalyst. An electrolyte was injected between both electrodes. Ruthenium complexes were used as sensitizers. These synthetic dyes have a good efficiency ranging from 11 to 12% and good thermal stability [2]. However, the production of this rare metal is costly and harmful to the environment. Therefore, the use of natural dyes is a new alternative. These dyes are abundant in nature, easy to extract, non-toxic and environmentally friendly. The dyes were extracted from leaves, barks, flowers, fruits, and used as molecular sensitizers. The dyes contain anthocyanins, betacyanins, carotenoid, tannins [3,4]. Several studies reported that natural dye sensitizers have been used successfully. Zhou et al., [5] studied natural dyes extracted from fruits and different parts of a plant. The extraction of mangosteen pulp with ethanol gave an efficiency of 1.17%. Moreover, Roy et al. [6] showed a short current density Jsc of 3.22 mA / cm², an open voltage Voc of 0.89 V and an efficiency of 2.09% using the Rose Bengal. Marco and Calogero [7] reported a conversion of 0.66%, using blood orange juice as a sensitizer. Wang et al. [8] realized the modification of coumarin structure to obtain derivatives that served as sensitizers. These sensitizers gave a conversion efficiency of 7.6%. However, DSSC efficiencies were stilled lower, compared to the other generation PV cells [9]. Researchers tried continually to overcome the issue of low efficiency in DSSC.

Senguta et al. reviewed several parameters to improve the photoanode performance in order to get high power conversion efficiency [10]. The photoanode film thickness and metal-TO₂ nanocomposites were found to be the ways to improve the efficiency. In DSSC, anode film thickness played an important role in the high generation of charge collection and reduction of the charge recombination rate [11]. Kumari et al. [12], studied the photovoltaic properties at different photoanode thicknesses and reported that 12 μm thickness was enough to enhance the photovoltaic activity.

In this paper, we explored a relatively simple and less expensive method to develop DSSC cells using a fraction extracted from Rauvolfia vomitoria fruit, a local plant Moreover, we studied the performance of DSSC obtained. Titanium dioxide (TiO₂), which provided a wide band gap, served as an electron transport to produce DSSC cells. We reported the I-V characteristic performances by varying the film thicknesses. The optical properties of the dye were studied with UV-Vis absorption spectroscopy and Fourier Transform Infrared spectroscopy (FT-IR). Cyclic voltammetry (CV) was used to estimate energy levels. The morphology of the TiO₂ surface was observed using a scanning electron microscope (SEM). The optoelectronic parameters of DSSC were obtained through exposure to the illumination of a halogen lamp of 78 mW / cm².

2. Experimental Details

2.1. Materials

Titanium dioxide TiO₂ (Ti-nanoxide, T / SP), and platinum (platisol, T / SP) were used to make electrodes. TC030 glass, has a thickness of 3mm and a resistivity of 15Ω/square. Both electrodes were sealed with a thermoplastic (Meltonix 1170-60/60). The electrolyte (AN-50) containing I⁻/ I³⁻ was injected into the space between both electrodes. All these materials were obtained from Solaronix Switzerland. Anhydrous acetonitrile, with a purity of 98%, is from Aldrich. It was associated with tetrabutylammonium tetrafluoroborate (TBATFB) obtained from Acros for cyclic voltammetry measurements.

Figure 1. Diagram of dye sensitized solar cell components

2.2. Apparatus and Instruments

Voltammograms of various registered dyes used acetonitrile solution with 0.1M tetrabutylammonium tetrafluoroborate as electrolyte. Measurements were made with a Palmsens potentiostat whose working electrode was a platinum disc with Ag / AgCl as the reference electrode, and a platinum wire as counter-electrode.

The acquisition of current-voltage density (J-V) was done with an Arduino microcontroller coupled with a computer and a halogen illumination lamp of 78 mW / cm². UV-Vis absorption was measured using JENWAY (7315, Germany) spectrometer. FTIR spectrum was recorded with PERKIN ELMER (Spectrum 65, UK) spectrometer. The surface morphology of TiO₂ and the thickness were carried out with a scanning electron microscope (SEM, HIROX, model SH 4000 M, France).

2.3. Dye Extraction

The dyes were extracted from the fruits of Rauvolfia vomitoria, a local plant. The ripe fruits were washed with water to remove dust particles and then grounded with a super blender to obtain a paste. Then, 100g of the resulting paste was extracted three times by maceration with 1000 mL of acetone (1:10, m/V) at 25°C. The obtained sample was filtered with filter paper (Whatman), then concentrated to dryness under vacuum at 40°C using a rotary evaporator. The resulting concentrated was dissolved in water and successively with hexane and ethyl acetate. After evaporation, the fraction of hexane was used as a dye.

2.4. Preparation of TiO₂ Photo Anode and Platinum Counter Electrode

The fluorine-doped tin oxide (2.5 cm, 2.5 cm, 0.3 cm) conductive glass (TC030) was cleaned with acetone and ethanol for 10 minutes. The nanocrystalline film preparation was carried out with the titanium dioxide paste (Ti-nanoxide T / sp). TiO₂ paste was then deposited on the conductive FTO glass side according to Doctor Blade’s method. Scotch tape was used to provide non-contact areas for electrical contact. After an air drying, TiO₂-coated plate was heated at 80 ° C for 5 minutes, then gradually at 450° C for 40 minutes with a hot plate. Next, TiO₂ electrode was removed from the hot plate and cooled down. TiO₂ coated glass with an active surface of 1 cm² was immersed into the dye extract for 24 h. At the end of the adsorption, TiO₂ film was removed from the solution and dried up for 15 min. In parallel, the platinum counter electrode (T / SP) was prepared with the other conductive glass electrode and annealed at a temperature of 400°C for one hour.

2.5. DSSC Assembling

In order to investigate the dye on TiO₂ thin film electrode performance, sandwich type cells with 1 mm of hole were made on platinum coated electrode. The first step was to isolate the active layer of TiO₂ by the sealing material (Meltonix 1170-60, 60 microns thickness). The photoanode which contains the dye was brought into contact with the platinum-coated counter-electrode and put on a hot plate. Subsequently, both electrodes were sealed by raising the temperature to 120 ° C in a few seconds. The open hole was used to inject the electrolyte (AN 50). The final step was to close the hole using the thermoplastic and a glass cover. A copper wire was glued to each electrode with the silver glue, to collect charges. Samples were made with various thicknesses of photoanode. DSSC cell was placed in the dark before any measurement.

3. Results and Discussion

3.1. Surface Morphology of TiO₂ Electrode

Figure 2 shows a porous structure of TiO₂ with various holes. The dye fill the different holes. This connection permits the transfer of the electron from the dye to the TiO₂ semiconductor. However, the morphologies are directly related to the thickness film. The smoothest surfaces were observed on the titanium electrode without crack for low thicknesses. As the thickness increases, cracks and roughness appear [11,12,13].

Figure 2. Rauvolfia v. dye adsorbed on TiO₂

3.2. Dye Absorption Spectrum

The absorbance of the dye extracted from Rauvolfia v., observed in Figure 3 indicates a high absorption between 400 nm and 500 nm, in the visible range. An examination of Figure 3 reveals that a peak appears at 459.25 nm and 486.33 nm. Similarly, the absorption band corresponds to carotenoid pigments, as reported [14,15]. Due to their absorbance, carotenoids are candidates for DSSC sensitization [16,17]. The presence of carbonyl and hydroxyl groups in their structure allows them to adhere easily to titanium dioxide and facilitate photovoltaic conversion [18].

Figure 3. Absorption spectrum of Rauvolfia v. dye

3.3. Fourier Transform Infrared Spectroscopy (FT-IR)

FT-IR spectroscopic analysis in Figure 4, revealed the presence of three bands, one weak and two strong bands between 3000.4 and 2851.9 cm⁻¹, attributed to aliphatic C-H stretching vibration of CH₂ and CH₃ groups. The bands observed at 1464.34 and 1377.60 cm⁻¹ confirmed the presence of CH₂ and CH₃ groups, respectively. The spectrum also indicated the presence of a strong absorption band at 1742.1 cm⁻¹ corresponding to carbonyl moiety of ester function and was confirmed by the presence of a band characteristic of aliphatic C-O bond at 1118.5 cm-1.

The presence of the bands at 1118.5 cm⁻¹ on the one hand and 1161.59 cm⁻¹ on the other can be assigned to the presence of the aromatic bond. The fraction of Rauvolfia dye has the following characteristic groups of ester, carbonyl (C = O) and will be adsorbed to TiO₂ thin layer.

Figure 4. FTIR spectrum of Rauvolfia v. dye

3.4. Electrochemical Study of the Dye

HOMO and LUMO energy levels of the dye fraction were evaluated in the cyclic voltammetry method. In this context, the working electrode is a platinum disc of 3mm of diameter with Ag / AgCl as the reference electrode and a platinum wire counter electrode. Tetrabutylammonium tetrafluoroborate (TBATFB) at 0.1 M was used as the supporting electrolyte in acetonitrile solution. Before any measurement, the electrolyte was purged with argon. The scanning speed was 50mV/s and the potential window was -2v to 2v. LUMO and HOMO levels were estimated according to the relations (1) and (2):

[picture] | (1)

[picture] | (2)

Where: Eox and Ered are respectively the oxidation and reduction potentials of the extract taken from the voltammograms (Figure 5) which show reversible cycles.

Following the oxidation and reduction potentials, the calculated HOMO and LUMO levels are 4.98 eV and 2.56 eV respectively. LUMO level of the dyes is above the potential 4.4 eV of I⁻/ I³⁻ redox couple electrolyte and indicates that, there is a driving force for the dye generation

Besides, HOMO energy level of the dye is higher compared to the TiO₂ extraction work (3.2 eV). These different HOMO and TiO₂ energy positions indicate that electron transfer from the dye to TiO₂ is possible.

Figure 5. Cyclic voltammogram of Rauvolfia v. dye in acetonitrile solution containing 0.1 M TBATFB supporting electrolyte at 50 mV/s rate

3.4. Effect of the Photoanode Thicknesses on the Performance of the Dye Solar Cell

The performances of the dye solar cells (DSSC) were evaluated with the photovoltaic parameters. In the dark, we observed negligible open-circuit voltage (Voc) and current density. The conversion efficiency (η) and the fill factor (FF) were calculated according to the following relations:

[picture] | (3)

[picture] | (4)

where, Jsc is the short-circuit current density, (Jmax) is the maximum current density, Vmax is the maximum voltage, Voc is the open-circuit voltage were determined from the (J-V) curve in Figure 6 and the incident light intensity (Pin). The photoelectric parameters of the cells from different photoanode films are listed in Table 1.

As seen from Figure 6 and Table 1, the short-circuit current density (Jsc) increases abruptly with increasing thickness from 5μm to 10μm, and then gradually decreases afterward. Variations in Jsc can be explained by the generation of photons. An increase in electrode thickness will directly increase the internal pore surface area and absorption capacity of the dye. Therefore, a thicker electrode can absorb more photons, leading to a higher Jsc. However, if the electrode thickness is greater than the depth of light penetration, the number of photons useful for electron generation will reach a limit and, therefore, Jsc cannot be increased beyond the penetration depth, resulting in more recombination centres and electron losses [13,14,15,16,17,18,19]. Besides, Voc decrease by increasing thickness, related to the back transfer of the electron between I₃⁻ ions and the conduction band electrons in TiO₂ electrode [20]. Thus, the optimum thickness was, 10 μm to achieve a higher photocurrent and power conversion efficiency of 0.055%. Dye extracted from saffron (0.06%) [21], lycopene(0.057%) [22], gave a similar efficiency matched to our dye. However, the power conversion of DSSC made with natural dye remained low compared to the stable complexed ruthenium [23].

Table 1. Photovoltaic parameters of DSSC for TiO₂ films

Figure 6. I-V characteristic of different TiO₂ films

4. Conclusion

The study showed the effect of various photoanode thicknesses on the photovoltaic response of dye solar cells (DSSC) using Rauvolfia Vomitoria fruit extract as a natural sensitizer. The obtained DSSC with 10 μm of TiO₂ thin film exhibited good photovoltaic properties. The highest photocurrent and power conversion efficiency achieved, were respectively 0.1 mA/cm² and 0.055%. Despite their fair efficiency, the natural dyes used in DSSC cells are promising. These dyes are easy to elaborate, and environmentally friendly.

References

[1]   | B. O’Regan et M. Grätzel, “A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films”, Nature, vol. 353, n 6346, p. 737-740, Oct. 1991.
[2]   | Y. Chiba, A. Islam, Y. Watanabe, R. Komiya, N. Koide, et L. Han, “Dye-sensitized solar cells with conversion efficiency of 11.1%”, Jpn. J. Appl. Phys., vol. 45, n 7L, p. L638, 2006.
[3]   | G. Calogero, J.-H. Yum, A. Sinopoli, G. Di Marco, M. Grätzelb, et M. K. Nazeeruddinb, “Anthocyanins and betalains as light-harvesting pigments for dye-sensitized solar cells”, Sol. Energy, vol. 86, p. 1563-1575, 2012.
[4]   | N. M. Gómez-Ortíz, I. A. Vázquez-Maldonado, A. R. Pérez-Espadas, G. J. Mena-Rejón, J. A. Azamar-Barrios, et G. Oskam, “Dye-sensitized solar cells with natural dyes extracted from achiote seeds”, Sol. Energy Mater. Sol. Cells, vol. 94, n 1, p. 40-44, Jan. 2010.
[5]   | H. Zhou, L. Wu, Y. Gao, et T. Ma, “Dye-sensitized solar cells using 20 natural dyes as sensitizers”, J. Photochem. Photobiol. Chem., vol. 219, n 2, p. 188-194, Apr. 2011.
[6]   | M. S. Roy, P. Balraju, M. Kumar, et G. D. Sharma, “Dye-sensitized solar cell based on Rose Bengal dye and nanocrystalline TiO2”, Sol. Energy Mater. Sol. Cells, vol. 92, n 8, p. 909-913, Aug. 2008.
[7]   | G. Calogero et G. Di Marco, “Red Sicilian orange and purple eggplant fruits as natural sensitizers for dye-sensitized solar cells”, Sol. Energy Mater. Sol. Cells, vol. 92, n 11, p. 1341-1346, 2008.
[8]   | Z.-S. Wang, Y. Cui, Y. Dan-oh, C. Kasada, A. Shinpo, et K. Hara, “Molecular Design of Coumarin Dyes for Stable and Efficient Organic Dye-Sensitized Solar Cells”, J. Phys. Chem. C, vol. 112, n 43, p. 17011-17017, Oct. 2008.
[9]   | K. Yoshikawa et al., “Silicon heterojunction solar cell with interdigitated back contacts for a photoconversion efficiency over 26%”, Nat. Energy, vol. 2, p. 17032, 2017.
[10]   | D. Sengupta, P. Das, B. Mondal, et K. Mukherjee, “Effects of doping, morphology and film-thickness of photo-anode materials for dye sensitized solar cell application–A review”, Renew. Sustain. Energy Rev., vol. 60, p. 356-376, 2016.
[11]   | A. Sedghi et H. N. Miankushki, “The effect of drying and thickness of TiO2 electrodes on the photovoltaic performance of dye-sensitized solar cells”, Int J Electrochem Sci, vol. 10, p. 3354-3362, 2015.
[12]   | J. Kumari, N. Sanjeevadharshini, M. Dissanayake, G. K. R. Senadeera, et C. A. Thotawatthage, “The effect of TiO2 photo anode film thickness on photovoltaic properties of dye-sensitized solar cells”, Ceylon J. Sci., vol. 45, n 1, 2016.
[13]   | B. C. Ferreira, D. M. Sampaio, R. Suresh Babu, et A. L. F. de Barros, “Influence of nanostructured TiO2 film thickness in dye-sensitized solar cells using naturally extracted dye from Thunbergia erecta flowers as a photosensitizer”, Opt. Mater., vol. 86, p. 239-246, Dec. 2018.
[14]   | E. Yamazaki, M. Murayama, N. Nishikawa, N. Hashimoto, M. Shoyama, et O. Kurita, “Utilization of natural carotenoids as photosensitizers for dye-sensitized solar cells”, Sol. Energy, vol. 81, n 4, p. 512-516, Apr. 2007.
[15]   | I. C. Maurya, Neetu, A. K. Gupta, P. Srivastava, et L. Bahadur, “Callindra haematocephata and Peltophorum pterocarpum flowers as natural sensitizers for TiO2 thin film based dye-sensitized solar cells”, Opt. Mater., vol. 60, p. 270-276, Oct. 2016.
[16]   | T. Maoka, “Recent progress in structural studies of carotenoids in animals and plants”, Arch. Biochem. Biophys., vol. 483, n 2, p. 191-195, 2009.
[17]   | S. Hao, J. Wu, Y. Huang, et J. Lin, “Natural dyes as photosensitizers for dye-sensitized solar cell”, Sol. Energy, vol. 80, n 2, p. 209-214, 2006.
[18]   | M. A. M. Al-Alwani, A. B. Mohamad, Abd. A. H. Kadhum, et N. A. Ludin, “Effect of solvents on the extraction of natural pigments and adsorption onto TiO2 for dye-sensitized solar cell applications”, Spectrochim. Acta. A. Mol. Biomol. Spectrosc., vol. 138, p. 130-137, Mar. 2015.
[19]   | C. Kim et al., “The effect of TiO2-coating layer on the performance in nanoporous ZnO-based dye-sensitized solar cells”, J. Power Sources, vol. 232, p. 159-164, 2013.
[20]   | M. C. Kao, H. Z. Chen, S. L. Young, C. Y. Kung, et dan C. Lin, “The effects of the thickness of TiO2 films on the performance of dye-sensitized solar cells”, Thin Solid Films, vol. 517, n 17, p. 5096-5099, 2009.
[21]   | M. Khalili, M. Abedi, et H. S. Amoli, “Influence of saffron carotenoids and mulberry anthocyanins as natural sensitizers on performance of dye-sensitized solar cells”, Ionics, vol. 23, n 3, p. 779-787, 2017.
[22]   | S. K. Srivastava, P. Piwek, S. R. Ayakar, A. Bonakdarpour, D. P. Wilkinson, et V. G. Yadav, “Biogenic Photovoltaics: A Biogenic Photovoltaic Material (Small 26/2018)”, Small, vol. 14, n 26, p. 1870121, 2018.
[23]   | H. A. Maddah, V. Berry, et S. K. Behura, “Biomolecular photosensitizers for dye-sensitized solar cells: Recent developments and critical insights”, Renew. Sustain. Energy Rev., vol. 121, p. 109678, 2020.